TY - JOUR
T1 - Impact of Environmental Stresses on the Antibacterial Activity of Graphene Oxide (GO) Nanoparticles against P. putida Biofilms
AU - Fallatah, Hussam
AU - Overton, Tim
AU - Ali-Boucetta, Hanene
AU - Gkatzionis, Kostas
PY - 2023/2/28
Y1 - 2023/2/28
N2 - As the production of graphene-based nanomaterials such as GO is increasing, it is expected that a large amount of GO waste will be generated. The environment (i.e., soil and aquatic systems) will be amongst the final repositories of these wastes which means important natural microbial communities in such environments will be at risk of GO exposure. However, little is known about how these communities respond to environmental stresses in synergy with the presence of GO. In this study, the effect of three different stress conditions: temperature (5, 25 and 40 °C); pH (5 to 9) and osmotic stress (51, 219 and 320 mM NaCl) in addition to GO treatment was investigated on the viability and physiology of biofilms and planktonic cells of soil bacterium P. putida. It was found that planktonic cells were more resistant to GO alone compared to biofilms. However, the cells were sensitive to GO when exposed to pH or osmotic stresses. Temperature was not found to influence the survival of biofilm with or without exposure to GO. However, low pH caused a reduction in colony-forming units (CFU) at pHs 5 and 6 for the pre-treated samples, while biofilms at pH 7–9 did not show any decrease. Interestingly, the post-treatment of planktonic cells or biofilms with GO showed a significant reduction in CFU at all pH ranges. The effect of higher osmotic stress in combination with GO resulted in a significant reduction in biofilms. These results show that the effect of stresses naturally occurring in the environment can be affected and changed when in combination with GO and can potentially affect the balance of natural biofilms.
AB - As the production of graphene-based nanomaterials such as GO is increasing, it is expected that a large amount of GO waste will be generated. The environment (i.e., soil and aquatic systems) will be amongst the final repositories of these wastes which means important natural microbial communities in such environments will be at risk of GO exposure. However, little is known about how these communities respond to environmental stresses in synergy with the presence of GO. In this study, the effect of three different stress conditions: temperature (5, 25 and 40 °C); pH (5 to 9) and osmotic stress (51, 219 and 320 mM NaCl) in addition to GO treatment was investigated on the viability and physiology of biofilms and planktonic cells of soil bacterium P. putida. It was found that planktonic cells were more resistant to GO alone compared to biofilms. However, the cells were sensitive to GO when exposed to pH or osmotic stresses. Temperature was not found to influence the survival of biofilm with or without exposure to GO. However, low pH caused a reduction in colony-forming units (CFU) at pHs 5 and 6 for the pre-treated samples, while biofilms at pH 7–9 did not show any decrease. Interestingly, the post-treatment of planktonic cells or biofilms with GO showed a significant reduction in CFU at all pH ranges. The effect of higher osmotic stress in combination with GO resulted in a significant reduction in biofilms. These results show that the effect of stresses naturally occurring in the environment can be affected and changed when in combination with GO and can potentially affect the balance of natural biofilms.
KW - graphene oxide
KW - biofilm
KW - P. putida
KW - environmental stresses
KW - toxicity
KW - Article
U2 - 10.3390/microorganisms11030609
DO - 10.3390/microorganisms11030609
M3 - Article
SN - 2076-2607
VL - 11
JO - Microorganisms
JF - Microorganisms
IS - 3
M1 - 609
ER -